ACI Global Home Middle East Region Portal Western Europe Region Portal
Email Address is required Invalid Email Address
In today’s market, it is imperative to be knowledgeable and have an edge over the competition. ACI members have it…they are engaged, informed, and stay up to date by taking advantage of benefits that ACI membership provides them.
Read more about membership
Learn More
Become an ACI Member
Topics In Concrete
Home > Frequently Asked Questions
In This Section
Frequently Asked Questions
Submit a Question
Search other resources on the ACI website for answers to technical questions
Q. Does the use of a pozzolan increase the mixing water requirement? A. In general, fly ash reduces the water requirement a few percent, whereas most other pozzolans increase it a few percent (ACI 232.R). Silica fume at high dosages will have a large effect in increasing the amount of water needed to achieve the desired workability because of the high surface area, but this is almost always compensated by using a high range water-reducing admixture (ACI 234R). Silica fume at low dosages (<5% by mass of cementitious material) reduces the water demand because it fills the voids between cement grains occupied by water displacing the trapped water. At high dosages, particle packing is complete for the most part and excess silica fume is adding more surface area, and thus increases the water demand. References: SP-1(02); E3-13 ; SP-221; ACI CT-23; ACI 232.1R-12; ACI 232.2R-03; ACI PRC-232.4-20; ACI 234R-06; ASTM C618; ASTM C1240 Topics in Concrete: Pozzolan; Cementitious Material; Materials in Concrete; Concrete Fundamentals
Q. Does the use of a pozzolan increase the mixing water requirement?
A. In general, fly ash reduces the water requirement a few percent, whereas most other pozzolans increase it a few percent (ACI 232.R). Silica fume at high dosages will have a large effect in increasing the amount of water needed to achieve the desired workability because of the high surface area, but this is almost always compensated by using a high range water-reducing admixture (ACI 234R). Silica fume at low dosages (<5% by mass of cementitious material) reduces the water demand because it fills the voids between cement grains occupied by water displacing the trapped water. At high dosages, particle packing is complete for the most part and excess silica fume is adding more surface area, and thus increases the water demand.
References: SP-1(02); E3-13 ; SP-221; ACI CT-23; ACI 232.1R-12; ACI 232.2R-03; ACI PRC-232.4-20; ACI 234R-06; ASTM C618; ASTM C1240
Topics in Concrete: Pozzolan; Cementitious Material; Materials in Concrete; Concrete Fundamentals