Title:
Optimization of Concrete Mixture Design and Cover Thickness for Reinforced Concrete Members under Chloride Exposure
Author(s):
Saeid A. Alghamdi, Shamsad Ahmad, and Adamu Lawan
Publication:
Materials Journal
Volume:
113
Issue:
5
Appears on pages(s):
589-598
Keywords:
chloride-induced reinforcement corrosion; corrosion current density; cover thickness; mixture design; optimization; reinforced concrete; service life
DOI:
10.14359/51689105
Date:
9/1/2016
Abstract:
This paper presents a methodology proposed based on experimental and analytical procedures for optimizing concrete mixture design parameters and concrete cover thickness to achieve specified service life of a reinforced concrete (RC) member subjected to severe chloride exposure conditions. To explain utility of the suggested methodology, an experimental work was conducted consisting of preparation, chloride exposure, and corrosion testing of RC specimens. Test specimens were decided based on an experimental design considering various key factors that included three major concrete mixture parameters with their three levels (27 mixtures), three concrete cover thicknesses, and three chloride exposures, making 243 combinations. Three replicates of each combination resulted in a total number of 729 test specimens that were allowed to corrode for a period of approximately 4 years under exposure to chloride solutions. Reinforcing bars were then extracted from specimens to determine the weight loss due to corrosion using the gravimetric method. The weight loss value for each specimen was converted into equivalent corrosion current density Icorr using Faraday’s law. The Icorr data were then analyzed statistically using Analysis of Variance (ANOVA) to study the effects of each factor on reinforcement corrosion rate. A customized regression model for Icorr was obtained to determine optimum levels of concrete mixture parameters and concrete cover thickness corresponding to Icorr,min for a specified chloride exposure. A procedure to calculate the service life against corrosion damage using Icorr,min was explained, which would help to ensure that a targeted service life is achieved.
Related References:
1. Bentur, A.; Diamond, S.; and Berke, N. S., Steel Corrosion in Concrete: Fundamentals and Civil Engineering Practice, E&FN Spon, London, UK, 1997, 208 pp.
2. ACI Committee 222, “Protection of Metals in Concrete against Corrosion (ACI 222R-01),” American Concrete Institute, Farmington Hills, MI, 2001, 41 pp.
3. Alghamdi, S. A., and Ahmad, S., “Multi-Criterion Optimal Designs of R/C Beams and Columns: Experimental and Analytical Studies,” KACST Research Project AT-23-21 Final Report, 2010.
4. Page, C. L., Corrosion of Reinforcement in Concrete Construction, The Royal Society of Chemistry, Cambridge, UK, 1996.
5. Kumar, V.; Singh, R.; and Quraishi, M. A., “A Study on Corrosion of Reinforcement in Concrete and Effect of Inhibitor on Service Life of RCC,” Journal of Materials and Environmental Science, V. 4, No. 5, 2013, pp. 726-731.
6. Park, J. I.; Bae, S. H.; Yu, K. G.; Lee, K. M.; and Choi, S., “Factors Influencing the Service Life of Concrete Structures Exposed to Coastal Environment,” The 3rd ACF International Conference-ACF/VCA, Ho Chi Minh City, Vietnam, Nov. 2008, pp. 1090-1095.
7. Güneyisi, E.; Gesoğlu, M.; Karaboğa, F.; and Mermerdaş, K., “Corrosion Behavior of Reinforcing Steel Embedded in Chloride Contaminated Concretes with and without Metakaolin,” Journal of Composites: Part B, V. 45, No. 1, 2013, pp. 1288-1295. doi: 10.1016/j.compositesb.2012.09.085
8. Oh, B. H.; Jang, B. S.; and Lee, S. C., “Chloride Diffusion and Corrosion Initiation Time of Reinforced Concrete Structures,” Proceedings of the International Workshop on Microstructure and Durability to Predict Service Life of Concrete Structures, Sapporo, Japan, Feb. 2004.
9. Abosrra, L.; Ashour, A. F.; and Youseffi, M., “Corrosion of Steel Reinforcement in Concrete of Different Compressive Strengths,” Construction and Building Materials, V. 25, No. 10, 2011, pp. 3915-3925. doi: 10.1016/j.conbuildmat.2011.04.023
10. Diab, A. M.; Elyamany, H. E.; and Abd Elmoty, A. M., “Effect of Mix Proportions, Seawater Curing Medium and Applied Voltages on Corrosion Resistance of Concrete Incorporating Mineral Admixtures,” Alexandria Engineering Journal, V. 50, No. 1, 2011, pp. 65-78. doi: 10.1016/j.aej.2011.01.013
11. Ali, S. I., “Effects of Aggregate Quality on Reinforcement Corrosion,” MSc thesis, Civil Engineering Department, King Fahd University of Petroleum and Minerals, Dhahran, Saudi Arabia, 2003.
12. Vennesland, Ø., and Havdahl, J., “Effect of Humidity and Chloride Content on the corrosion of Steel Embedded in LWA,” Materials and Corrosion, V. 60, No. 2, 2009, pp. 106-110. doi: 10.1002/maco.200805024
13. Sun, Y. L. S., and Zhu, J. S., “Effect of Water-Cement Ratio on Carbonation and Steel-Corrosion Resistance of Recycled Concrete,” Applied Mechanics and Materials, V. 174-177, 2012, pp. 1552-1557. doi: 10.4028/www.scientific.net/AMM.174-177.1552
14. Moon, K. M.; Cho, H.; Kim, Y.; Bae, S.; and Lee, M., “Effect of W/C and Thickness to Corrosion Properties of Reinforced Concrete,” Proceedings of the Eighteenth International Offshore and Polar Engineering Conference, Vancouver, BC, Canada, July 6-11, 2008, pp. 412-416.
15. Moon, K. M.; Lee, S.; Lee, M.; and Kim, Y., “Effect of W/C Ratio and Cover Thickness on Polarization Characteristics of Embedded Steel in Mortar,” Journal of Transactions of Nonferrous Metals Society of China, V. 19, No. 4, 2009, pp. 909-912. doi: 10.1016/S1003-6326(08)60375-1
16. Shi, H.; Guo, X.; and Zhang, H., “Influence of Ratio of Water to Cement on Corrosion of Steel Bar in Hydraulic Concrete,” Journal of Hydraulic Engineering, V. 40, No. 12, 2009, pp. 1500-1505.
17. Lee, S. Y.; Won, J. P.; Park, D. H.; Lee, M. H.; and Moon, K. M., “The Effect of Cover Thickness to Corrosion Characteristics of Reinforced Steel Bar Embedded in Mortar Specimen (W/C: 0.6) Aged 5 Years in Seawater,” Journal of Advanced Materials Research, 2013, pp 1176-1180.
18. Kalabisová, E.; Turek, L.; Poddaná, M.; Biba, M.; and Cíhal, V., “Influence of Concrete Properties and Reinforcing bar Distribution on Measurements of Corrosion Rates of Embedded Steel,” 17th International Corrosion Congress 2008: Corrosion Control in the Service of Society, Las Vegas, NV, 2008, pp. 2559-2566.
19. Yu, H.; Lu, B.; Presuel-Moreno, F.; and Zheng, W., “Effects of Concrete Mix on Initiation of Reinforcement Corrosion and Chloride Threshold Level,” Journal of the Transportation Research Board, V. 2220, 2011, pp. 75-81. doi: 10.3141/2220-09
20. Medagoda Arachchige, A. D., “Influence of Cement Content on Corrosion Resistance,” Proceedings of the Institution of Civil Engineers: Construction Materials, V. 161, No. 1, 2008, pp. 31-39. doi: 10.1680/coma.2008.161.1.31
21. Román, J.; Vera, R.; Bagnara, M.; Carvajal, A. M.; and Aperador, W., “Effects of Chloride Ions on the Corrosion of Galvanized Steel Embedded in Concrete Prepared with Cements of Different Composition,” International Journal of Electrochemical Science, V. 9, 2014, pp. 580-592.
22. ACI Committee 201, “Guide to Durable Concrete Chemical Admixtures for Concrete (ACI 201.2R-01),” American Concrete Institute, Farmington Hills, MI, 2001, 48 pp.
23. ACI Committee 211, “Standard Practice for Selecting Proportions for Normal, Heavyweight, and Mass Concrete (ACI 211.1-91),” Farmington Hills, MI, 1991, 49 pp.
24. Rasheeduzaffar; Dakhil, F. H.; and Bader, M. A., “Toward Solving the Concrete Deterioration Problem in the Arabian Gulf Region,” Arabian Journal for Science and Engineering, V. 11, No. 2, 1986, pp. 129-146.
25. Shameem, M.; Maslehuddin, M.; Saricimen, H.; and Al-Mana, A. I., “Extending the Life of RC Structures in the Arabian Gulf Environment,” Proceedings of Conference on Structural Faults and Repair, London, UK, July 1995.
26. Gjorv, O. E., “Durability of Concrete Containing Condensed Silica Fume,” Fly Ash, Silica Fume, Slag and Other Mineral By-Products in Concrete, SP-79, American Concrete Institute, Farmington Hills, MI, 1983, pp. 695-708.
27. Hussain, S. E., “Mechanisms of High Durability Performance of Plain and Blended Cements,” PhD thesis, Civil Engineering Department, King Fahd University of Petroleum and Minerals, Dhahran, Saudi Arabia, 1991.
28. Kumar, A.; Komarneni, S.; and Roy, D. M., “Diffusion of K+ and Cl– through Sealing Materials,” Cement and Concrete Research, V. 17, No. 1, 1987, pp. 153-160. doi: 10.1016/0008-8846(87)90069-X
29. Maslehuddin, M., “Optimization of Concrete Mix Design for Durability in the Eastern Province of Saudi Arabia,” MS thesis, Civil Engineering Department, King Fahd University of Petroleum and Minerals, Dhahran, Saudi Arabia, 1981.
30. Soudki, K. A.; El-Salakawy, E. F.; and Elkum, N. B., “Full Factorial Optimization of Concrete Mix Design for Hot Climates,” Journal of Materials in Civil Engineering, ASCE, V. 13, No. 6, 2001, pp. 427-433. doi: 10.1061/(ASCE)0899-1561(2001)13:6(427)
31. McDonald, D., “Design Options for Corrosion Protection,” Concrete 95—Toward Better Concrete Structures, Concrete Institute of Australia, 1995, pp. 75-83.
32. ACI Committee 201, “Guide to Durable Concrete (ACI 201.2R-77),” American Concrete Institute, Farmington Hills, MI, 1977.
33. ACI Committee 318, “Building Code Requirements for Structural Concrete (ACI 318-05) and Commentary,” American Concrete Institute, Farmington Hills, MI, 2005, 430 pp.
34. Hong, K., and Hooton, R. D., “Effects of Cyclic Chloride Exposure on Penetration of Concrete Cover,” Cement and Concrete Research, V. 29, No. 9, 1999, pp. 1379-1386. doi: 10.1016/S0008-8846(99)00073-3
35. Al-Kutti, W. A., “Compliance Criteria for Quality Concrete,” MS thesis, Civil & Environmental Engineering Department, King Fahd University of Petroleum & Minerals, Dhahran, Saudi Arabia, May 2005.
36. Mangat, P. S., and Elgarf, M. S., “Flexural Strength of Concrete Beams with Corroding Reinforcement,” ACI Structural Journal, V. 96, No. 1, Jan.-Feb. 1999, pp. 149-158.
37. Jin, W., and Zhao, Y., “Effect of Corrosion on Bond Behavior and Bending Strength of Reinforced Concrete Beams,” Journal of Zhejiang University. Science, V. 2, No. 3, 2001, pp. 298-308. doi: 10.1631/jzus.2001.0298
38. Azad, A. K.; Ahmad, S.; and Azher, S. A., “Residual Strength of Corrosion-Damaged Reinforced Concrete Beams,” ACI Materials Journal, V. 104, No. 1, Jan.-Feb. 2007, pp. 40-47.
39. Azad, A. K.; Ahmad, S.; and Al-Gohi, B. H. A., “Flexural Strength of Corroded Reinforced Concrete Beams,” Magazine of Concrete Research, V. 62, No. 6, 2010, pp. 405-414. doi: 10.1680/macr.2010.62.6.405
40. ASTM G1-03, “Standard Practice for Preparing, Cleaning, and Evaluating Corrosion Test Specimens,” ASTM International, West Conshohocken, PA, 2003, 9 pp.
41. Ijsseling, F. P., “Application of Electrochemical Methods of Corrosion Rate Determination to System Involving Corrosion Product Layers,” British Corrosion Journal, V. 21, No. 2, 1986, pp. 95-101. doi: 10.1179/000705986798272316