Title:
Incorporating Cracks in Chloride Ingress Modeling and Service Life Predictions
Author(s):
Jose Pacheco
Publication:
Materials Journal
Volume:
116
Issue:
5
Appears on pages(s):
113-118
Keywords:
chloride exposure; concrete cracking; service life
DOI:
10.14359/51716832
Date:
9/1/2019
Abstract:
The presence of uncontrolled or unexpected nonstructural cracking in reinforced concrete structures generally leads to conflict and disputes. The current industry practice aims to prevent or mitigate the presence of cracking at early ages (that is, plastic shrinkage, thermally induced cracking) or due to volumetric changes (restrained or drying shrinkage). However, cracking of concrete can still occur and lead to questioning the durability of concrete with prolonged service life expectations such as bridge decks, piers, or waterfront structures, to name a few. The effect of cracks on chloride penetration has been thoroughly studied, and evidence of the effect of cracks on accelerated ingress of chlorides is well established. Structural codes and guides, on the other hand, consider that the integrity of the concrete element is not significantly affected as long as the crack width does not exceed a recommended limit based on exposure conditions. Similarly, service life predictions based on chloride ingress modeling disregard the effect of cracks. Because crack-free concrete cannot be guaranteed, service life predictions that neglect the effect of cracks can be significantly inaccurate. A simplified approach is presented in this paper, where a correction to the chloride diffusion coefficient of concrete is performed to account for the effect of cracks. This correction is similar, in principle, to the so-called aging or decay coefficient in concrete. Results of Monte Carlo simulations on chloride ingress and estimations of the time-to-corrosion initiation are presented and discussed. Results indicate that a decrease of the reliability index (β), or an increase in the probability of failure (pf), can be calculated when accounting for the effect of cracks.
Related References:
1. Tuutti, K., Corrosion of Steel in Concrete, Swedish Cement and Concrete Research Institute, Stockholm, Sweden, 1982.
2. Kosmatka, S. H., and Wilson, M. L., Design and Control of Concrete Mixtures, Portland Cement Association, Skokie, IL, 2016.
3. Bertolini, L.; Elsener, B.; Pedeferri, P.; Redaelli, E.; and Polder, R. B., Corrosion of Steel in Concrete: Prevention, Diagnosis, Repair, John Wiley & Sons, Inc., New York, 2013.
4. “Non-Structural Cracks in Concrete,” Report of a Concrete Society Working Party, Concrete Society London, London, UK, 1992.
5. Nilsson, L. O., “WP4 Report – Modelling of Chloride Ingress. CHLORTEST–EU Funded Research Project, “Resistance of Concrete to Chloride Ingress–From Laboratory Tests to In-Field Performance,” G6RD-CT-2002-0085, Deliverables D14-15, 2005.
6. ACI Committee 224, “Control of Cracking in Concrete Structures (ACI 224R-01),” American Concrete Institute, Farmington Hills, MI, 2001, 43 pp.
7. Pacheco, J.; Šavija, B.; Schlangen, E.; and Polder, R. B., “Assessment of Cracks in Reinforced Concrete by Means of Electrical Resistance and Image Analysis,” Construction and Building Materials, V. 65, 2014, pp. 417-426. doi: 10.1016/j.conbuildmat.2014.05.001
8. Šavija, B.; Pacheco, J.; and Schlangen, E., “Lattice Modeling of Chloride Diffusion in Sound and Cracked Concrete,” Cement and Concrete Composites, V. 42, 2013, pp. 30-40. doi: 10.1016/j.cemconcomp.2013.05.003
9. Šavija, B.; Schlangen, E.; Pacheco, J.; Millar, S.; Eichler, T.; and Wilsch, G., “Chloride Ingress in Cracked Concrete: A Laser Induced Breakdown Spectroscopy (LIBS) Study,” Journal of Advanced Concrete Technology, V. 12, No. 10, 2014, pp. 425-442. doi: 10.3151/jact.12.425
10. Djerbi, A.; Bonnet, S.; Khelidj, A.; and Baroghel-Bouny, V., “Influence of Traversing Crack on Chloride Diffusion Into Concrete,” Cement and Concrete Research, V. 38, No. 6, 2008, pp. 877-883. doi: 10.1016/j.cemconres.2007.10.007
11. Boulfiza, M.; Sakai, K.; and Banthia, N., “Prediction of Chloride Ions Ingress in Uncracked and Cracked Concrete,” ACI Materials Journal, V. 100, No. 1, Jan.-Feb. 2003, pp. 38-48.
12. Win, P.; Watanabe, M.; and Machida, A., “Penetration Profile of Chloride Ion in Cracked Reinforced Concrete,” Cement and Concrete Research, V. 34, No. 7, 2004, pp. 1073-1079. doi: 10.1016/j.cemconres.2003.11.020
13. Gowripalan, N.; Sirivivatnanon, V.; and Lim, C. C., “Chloride Diffusivity of Concrete Cracked in Flexure,” Cement and Concrete Research, V. 30, No. 5, 2000, pp. 725-730. doi: 10.1016/S0008-8846(00)00216-7
14. Marsavina, L.; Audenaert, K.; De Schutter, G.; Faur, N.; and Marsavina, D., “Experimental and Numerical Determination of the Chloride Penetration in Cracked Concrete,” Construction and Building Materials, V. 23, No. 1, 2009, pp. 264-274. doi: 10.1016/j.conbuildmat.2007.12.015
15. Konin, A.; Francois, R.; and Arliguie, G., “Penetration of Chlorides in Relation to the Microcracking State Into Reinforced Ordinary and High Strength Concrete,” Materials and Structures, V. 31, No. 5, 1998, pp. 310-316. doi: 10.1007/BF02480672
16. Otieno, M. B.; Alexander, M. G.; and Beushausen, H. D., “Corrosion in Cracked and Uncracked Concrete—Influence of Crack Width, Concrete Quality and Crack Reopening,” Magazine of Concrete Research, V. 62, No. 6, 2010, pp. 393-404. doi: 10.1680/macr.2010.62.6.393
17. Balakumaran, S. S.; Weyers, R. E.; and Brown, M. C., “Influence of Cracks on Corrosion Initiation in Bridge Decks,” ACI Materials Journal, V. 114, No. 1, Jan.-Feb. 2017, doi: 10.14359/51689489
18. Jaffer, S. J., and Hansson, C. M., “Chloride-Induced Corrosion Products of Steel in Cracked-Concrete Subjected to Different Loading Conditions,” Cement and Concrete Research, V. 39, No. 2, 2009, pp. 116-125. doi: 10.1016/j.cemconres.2008.11.001
19. Schießl, P., and Raupach, M., “Laboratory Studies and Calculations on the Influence of Crack Width on Chloride-Induced Corrosion of Steel in Concrete,” ACI Materials Journal, V. 94, No. 1, Jan.-Feb. 1997, pp. 56-61.
20. Bastidas-Arteaga, E.; Sánchez-Silva, M.; Chateauneuf, A.; and Silva, M. R., “Coupled Reliability Model of Biodeterioration, Chloride Ingress and Cracking for Reinforced Concrete Structures,” Structural Safety, V. 30, No. 2, 2008, pp. 110-129. doi: 10.1016/j.strusafe.2006.09.001
21. Pacheco, J., and Polder, R. B., “Corrosion Initiation and Propagation in Cracked Concrete—A Literature Review,” Advances in Modeling Concrete Service Life, 2012, Springer, Dordrecht, pp. 85-93.
22. ACI Committee 231, “Report on Early-Age Cracking: Causes, Measurement, and Mitigation (ACI 231R-10),” American Concrete Institute, Farmington Hills, MI, 2010, 46 pp.
23. Dean, J., and Lange, N., Lange’s Handbook of Chemistry, McGraw-Hill Professional, New York City, 1998.