Title:
Enhancing Mechanical Properties of Alkali‑Activated Slag SIFCON for Sustainable Construction Using Recycled Glass and Tire‑Derived Waste Steel Fibers
Author(s):
Saadet Gokce Gok and Ozkan Sengul
Publication:
IJCSM
Volume:
19
Issue:
Appears on pages(s):
Keywords:
SIFCON, Alkali activation, Waste fibers, Scrap tires, Mechanical properties
DOI:
10.1186/s40069-024-00724-6
Date:
3/31/2025
Abstract:
This paper presents the outcomes of a study in which continuous steel fibers, recovered from scrap tires of vehicles,
were used to prepare alkali-activated slag-based slurry infiltrated fibrous concrete (SIFCON). In this experimental
study, the steel fibers used were 250 mm long, with varying fiber contents of 0%, 1%, 2%, 3%, 4%, and 5%. The
alkali-activated SIFCONs were produced by activating ground granulated blast furnace slag (GGBS) with a mixture
of sodium hydroxide (NaOH) and sodium silicate (
Na2SiO3) solutions. Mixtures with ordinary Portland cement (OPC)
were also cast for comparison purposes. The feasibility of utilizing finely ground waste glass as a silicate source
for chemical activator solution in alkali-activated SIFCONs was also investigated. In this context, two different
molar concentrations of NaOH, namely 8 M and 14 M, were employed during production. As activators, one series
of mixtures utilized sodium hydroxide and sodium silicate solutions, while the other series replaced sodium silicate
with finely ground waste glass. As a result, three different waste materials were utilized in concrete. 30 different
mixtures were cast and examined in the experimental study. Load–deflection curves were obtained in three-point
bending test and mechanical properties of the mixtures such as compressive, splitting and flexural strengths, fracture
energy, and toughness were determined. The flexural strength and toughness increased with the use of waste steel
fibers. The continuous waste fibers derived from discarded tires yielded results comparable to commercially available
fibers, demonstrating their effectiveness in enhancing mechanical properties. Depending on mix design, the alkaliactivated
SIFCON attained flexural strength exceeding 75 MPa and compressive strength surpassing 100 MPa. These
results suggest that concretes incorporating a variety of waste materials can be effectively combined. This innovative
approach bridges an existing gap in the literature by combining alkali activation, waste glass, and waste steel fibers,
ultimately yielding a sustainable composite that outperforms normal concretes in terms of mechanical properties
while promoting environmental sustainability. Test results demonstrate that it is possible to obtain concrete
with comparable mechanical properties while primarily composed of by-products and waste materials. This approach
marks a substantial step in achieving high-performance concrete that relies solely on waste or by-products.