Title:
Electrical Resistivity and Formation Factor of Air-Entrained Concrete
Author(s):
Chunyu Qiao, Mehdi Khanzadeh Moradllo, Hope Hall, M. Tyler Ley, and W. Jason Weiss
Publication:
Materials Journal
Volume:
116
Issue:
3
Appears on pages(s):
85-93
Keywords:
air content; apparent formation factor; electrical resistivity; formation factor; Nick Point
DOI:
10.14359/51714506
Date:
5/1/2019
Abstract:
This paper studies the influence of air content on the electrical resistivity and formation factor of concrete as these measures are often used in specifications for acceptance and payment. Experimental measurements are conducted on 30 air-entrained concretes with three water-cement ratios (w/c = 0.40, 0.45, and 0.50) over a large range of air contents (2.5 to 9.0%). The porosity of the concrete is measured, which is comparable to the theoretical estimation from the Powers-Brownyard model. Electrical resistivity measurements are performed on saturated concrete samples, and samples submerged in simulated pore solutions. The samples submerged in a bucket of simulated pore solution achieve a degree of saturation that relates to the filling of matrix pores, (that is, the Nick Point). The degree of saturation at the Nick Point (SNK) decreases as the air content increases. A formation factor (FSAT) is calculated for the saturated concrete, as well as the apparent formation factor FNK for the samples submerged which reach Nick Point saturation (SNK) in the simulated pore solution. As the air content increases, FSAT decreases due to the increased porosity (air voids) that are filled with conductive fluid, while FNK is independent on the air content (as the air voids are filled with nonconductive air). As the w/c increases, both FSAT and FNK decrease due to the increased porosity and connectivity. For the concrete with the same w/c, the addition of a high-range water-reducing admixture (HRWRA) results in higher values of FSAT and FNK due to the refined microstructure in mixtures containing HRWRA. A saturation function is used to provide a powerful tool in quality control to back-calculate FSAT that relates to different transport properties.
Related References:
1. Scherer, G. W., and Valenza, J. J., “Mechanisms of Frost Damage,” Materials Science of Concrete, V. VII, J. Skalny and J. F. Young, eds., American Ceramic Society, 2005, pp. 209-246.
2. ACI Committee 201, “Guide to Durable Concrete (ACI 201.2R-16),” American Concrete Institute, Farmington Hills, MI, 2016, 84 pp.
3. Powers, T. C., “Void Space as a Basis for Producing Air-Entrained Concrete,” ACI Journal Proceedings, V. 50, No. 5, May 1954, pp. 741-760.
4. Hover, K., “Some Recent Problems with Air-Entrained Concrete,” Cement, Concrete and Aggregates, V. 11, No. 1, 1989, pp. 67-72.
5. Maclnnis, C., and Becaudoin, J. J., “Effect of Degree of Saturation on the Frost Resistance of Mortar Mixes,” ACI Journal Proceedings, V. 65, No. 3, Mar. 1968, pp. 203-208.
6. Fagerlund, G., “The Signifcance of Critical Degrees of Saturation at Freezing of Porous and Brittle Materials,” Durability of Concrete, SP-47, C. F. Scholer and E. Farkas, eds., American Concrete Institute, Farmington Hills, MI, 1975, pp. 13-66.
7. Fagerlund, G., “The International Cooperative Test of the Critical Degree of Saturation Method of Assessing the Freeze/Thaw Resistance of Concrete,” Materiales de Construcción, V. 10, No. 4, 1977, pp. 231-253.
8. Bentz, D. P.; Ehlen, M. A.; Ferraris, C. F.; and Garboczi, E. J., “Sorptivity-Based Service Life Predictions for Concrete Pavements,” International Society for Concrete Pavements, Orlando, FL, 2001, pp. 181-193.
9. Fagerlund, G., “A Service Life Model for Internal Frost Damage in Concrete,” Report TVBM, V. 3119, Division of Building Materials, LTH, Lund University, Lund, Sweden, 2004.
10. Baroghel-Bouny, V.; Mainguy, M.; Lassabatere, T.; and Coussy, O., “Characterization and Identification of Equilibrium and Transfer Moisture Properties for Ordinary and High-Performance Cementitious Materials,” Cement and Concrete Research, V. 29, No. 8, 1999, pp. 1225-1238.
11. Li, W.; Pour-Ghaz, M.; Castro, J.; and Weiss, J., “Water Absorption and Critical Degree of Saturation Relating to Freeze-Thaw Damage in Concrete Pavement Joints,” Journal of Materials in Civil Engineering, ASCE, V. 24, No. 3, 2012, pp. 299-307.
12. Hall, C., and Hoff, W. D., “Topics in Water Transport,” Water Transport in Brick, Stone and Concrete, CRC Press, Boca Raton, FL, 2011, pp. 221-288.
13. Todak, H. N., “Durability Assessments of Concrete Using Electrical Properties and Acoustic Emission Testing,” Purdue University, West Lafayette, IN, 2015.
14. Wong, H. S.; Pappas, A. M.; Zimmerman, R. W.; and Buenfeld, N. R., “Effect of Entrained Air Voids on the Microstructure and Mass Transport Properties of Concrete,” Cement and Concrete Research, V. 41, No. 10, 2011, pp. 1067-1077.
15. Snyder, K. A., “The Relationship between the Formation Factor and the Diffusion Coefficient of Porous Materials Saturated with Concentrated Electrolytes: Theoretical And Experimental Considerations,” Concrete Science and Engineering, V. 3, No. 12, 2001, pp. 216-224.
16. Katz, A. J., and Thompson, A. H., “Quantitative Prediction of Permeability in Porous Rock,” Physical Review. B, V. 34, No. 11, 1986, pp. 8179-8181.
17. Moradllo, M. K.; Qiao, C.; Isgor, B.; Reese, S.; and Weiss, W. J., “Relating the Formation Factor of Concrete to Water Absorption,” ACI Materials Journal, V. 115, No. 6, Nov. 2018, pp. 887-898.
18. Qiao, C.; Coyle, A.; Isgor, B.; and Weiss, J., “Prediction of Chloride Ingress in Saturated Concrete Using Formation Factor and Chloride Binding Isotherm,” Advances in Civil Engineering Materials, V. 7, No. 1, 2018, pp. 206-220.
19. Spragg, R.; Qiao, C.; Barrett, T.; and Weiss, J., “Assessing a Concrete’s Resistance to Chloride Ion Ingress Using the Formation Factor,” Corrosion of Steel in Concrete Structures, Woodhead Publishing, Oxford, UK, 2016, pp. 211-238.
20. Weiss, J.; Suyder, K.; Bullard, J.; and Bentz, D., “Using a Saturation Function to Interpret the Electrical Properties of Partially Saturated Concrete,” Journal of Materials in Civil Engineering, ASCE, V. 25, No. 8, 2013, pp. 1097-1106.
21. Bu, Y., and Weiss, J., “Saturation of Air Entrained Voids and Its Implication on the Transport of Ionic Species in Concrete,” Purdue University, West Lafayette, IN, 2014, pp. 182-189.
22. Barrett, T. J., “Improving Service Life of Concrete Structures through the Use of Internal Curing: Impact on Practice,” Purdue University, West Lafayette, IN, 2015.
23. Weiss, W.; Barrett, T.; Qiao, C.; and Todak, H., “Toward a Specification for Transport Properties of Concrete Based on the Formation Factor of a Sealed Specimen,” Advances in Civil Engineering Materials, V. 5, No. 1, 2016, pp. 179-194.
24. Ley, M. T.; Welchel, D.; Peery, J.; Khatibmasjedi, S.; and LeFlore, J., “Determining the Air-Void Distribution in Fresh Concrete with the Sequential Air Method,” Construction and Building Materials, V. 150, 2017, pp. 723-737.
25. Bu, Y.; Spragg, R.; and Weiss, W. J., “Comparison of the Pore Volume in Concrete as Determined Using ASTM C642 and Vacuum Saturation,” Advances in Civil Engineering Materials, V. 3, No. 1, 2014, pp. 308-315.
26. AASHTO TP 119, “Standard Method of Test for Electrical Resistivity of a Concrete Cylinder Tested in a Uniaxial Resistance Test,” American Association of State Highway and Transportation Officials, Washington DC, 2015, 12 pp.
27. Spragg, R. P., “The Rapid Assessment of Transport Properties of Cementitious Materials Using Electrical Methods,” Purdue University, West Lafayette, IN, 2013.
28. Spragg, R.; Bu, Y.; Snyder, K. A.; Bentz, D. P.; and Weiss, J., “Electrical Testing of Cement-Based Materials: Role of Testing Techniques, Sample Conditioning, and Accelerated Curing,” Publication FHWA/IN/JTRP-2013/28. Joint Transportation Research Program, Indiana Department of Transportation and Purdue University, West Lafayette, IN, 2013. doi: 10.5703/1288284315230.
29. National Institute of Standards and Technology, “Estimation of Pore Solution Conductivity,” 2017, https://www.nist.gov/el/materials-and-structural-systems-division-73100/inorganic-materials-group-73103/estimation-pore. (last accessed May 16, 2019)
30. Powers, T. C., and Brownyard, T. L., “Studies of the Physical Properties of Hardened Portland Cement Paste,” Research Laboratories of the Portland Cement Association, Chicago, IL, 1948.
31. Castro, J.; Bentz, D.; and Weiss, J., “Effect of Sample Conditioning on the Water Absorption of Concrete,” Cement and Concrete Composites, V. 33, No. 8, 2011, pp. 805-813.
32. Sakai, E.; Kasuga, T.; Sugiyama, T.; Asaga, K.; and Daimon, M., “Influence of Superplasticizers on the Hydration of Cement and the Pore Structure of Hardened Cement,” Cement and Concrete Research, V. 36, No. 11, 2006, pp. 2049-2053.
33. Huang, H.; Qian, C.; Zhao, F.; Qu, J.; Guo, J.; and Danzinger, M., “Improvement on Microstructure of Concrete by Polycarboxylate Superplasticizer (PCE) and Its Influence on Durability of Concrete,” Construction and Building Materials, V. 110, 2016, pp. 293-299.
34. Francy, O., Modelling of Chloride Ions Ingress in Partially Water Saturated Mortars, Paul Sabatier University, Toulouse, France, 1998.
35. Olsson, N.; Baroghel-Bouny, V.; Nilsson, L.-O.; and Thiery, M., “Non-Saturated Ion Diffusion in Concrete—A New Approach to Evaluate Conductivity Measurements,” Cement and Concrete Composites, V. 40, 2013, pp. 40-47.